Resistance:Fixed Resistor
Material:Metal Film Resistor
Packaging:Throught Hole
Origin:Shenzhen city, China
Pak Heng Electronics Co.,Ltd is one of the leading metal oxide film fixed resistors manufacturers and suppliers in China, offering the free sample and competitive price. Welcome to wholesale the high quality bulk resistors made in China from us. It if of good performance and high safety.
Properties
Metal oxide film resistors exceed the performance of metal film and carbon film for the following properties: power rating, voltage rating, overload capabilities, surges and high temperatures. Designers choose often the metal oxide film resistor for high endurance applications. For an overview of resistor types with their properties, look here. Stability properties are less good than for the metal film resistor. The metal oxide film resistors have poor properties for low values and tolerance. The temperature coefficient is around 300 ppm/°C, which is higher than for metal film types.
The resistance material for metal oxide resistors is tin oxide that is contaminated with antimony oxide, this is to increase the resistivity. Metal oxide resistors can withstand higher temperatures than carbon or metal film resistors. The noise properties are similar to carbon resistors.
Part No. | Power | Resistance range | Dimensions | Max. orking voltage | Max.overload voltage | Max.Pulse voltage | Max.insulation voltage | ||
L±1 | D±0.5 | d±0.05 | |||||||
CMO016 MOR016 | 1/8W 1/6W | 0R~1M | 3.2 | 1.7 | 0.41 | 150V | 300V | 300V | 200V |
CMO14S MOR14S | 1/4Ws | 0R~1M | 3.2 | 1.7 | 0.41 | 150V | 300V | 300V | 200V |
CMO014 MOR014 | 1/4W | 0R~1M | 6.0 | 2.3 | 0.45 | 200V | 400V | 500V | 250V |
0.52 | |||||||||
CMO12S MOR12S | 1/2WS | 0R~1M | 6.0 | 2.3 | 0.45 | 200V | 400V | 500V | 250V |
0.52 | |||||||||
MOR012 | 1/2W | 0R1~1M | 9.0 | 3.2 | 0.52 | 250V | 400V | 500V | 250V |
MOR01S | 1WS | 0R1~1M | 9.0 | 3.2 | 0.58 | 350V | 600V | 750V | 350V |
MOR01B | 1W | 0R1~1M | 11.0 | 4.5 | 0.75 | 350V | 600V | 750V | 350V |
MOR02S | 2WS | 0R1~1M | 11.0 | 4.5 | 0.75 | 350V | 600V | 750V | 350V |
MOR02B | 2W | 0R1~1M | 15.0 | 5.0 | 0.75 | 350V | 600V | 750V | 350V |
MOR03S | 3WS | 0R1~1M | 15.0 | 5.0 | 0.75 | 350V | 600V | 750V | 350V |
MOR03B | 3W | 0R1~1M | 24.0 | 8.0 | 0.75 | 500V | 800V | 1000V | 500V |
MOR05S | 5WS | 0R1~1M | 24.0 | 8.0 | 0.75 | 500V | 800V | 1000V | 500V |
Test Item | Test Condition | Performance |
Temperature coefficient | Test the resistance value at normal temperature and normal temperature added 100?,calculate per? resistance value change rate . | ±350ppm/? |
Short time overload | 2.5 × rated voltage or Max.overload voltage (get the lower) for 5 seconds. | ?R=±(1%R0+0.05O) |
Pulse overload | At 4 x rated voltage or Max. pulse overload voltage (get the lower) cycle 10000±200 times(1 second on, 25 seconds off ). | ?R=±(2%R0+0.05O) |
Resistance to soldering heat | Immerge into 350±10? tin stove for 2~3 seconds. | ?R=±(1%R0+0.05O) |
Solderability | Immerge into 245±3? tin stove for 2~3 seconds. | The area of soldering is over 95% |
Temperature cycling | At -55? for 30 min, then at +25? for 10~15 min, then at +125? for 30 min, then at +25? for 10~15 min, total 5 cycles. | ?R=±(1%R0+0.05O) |
Load life in humidity | Overload rated voltage or Max.working voltage (get the lower) for 1000 hours (1.5 hours on and half-hour off ) at the 40±2? and 90~95% relative humidity. | ?R=±(5%R0+0.05O) |
Load life in heat | Overload rated voltage or Max.working voltage (get the lower ) for 1000 hours (1.5 hours on and half-hour off) at the 70±2?. | ?R=±(5%R0+0.05O) |
Nonflammability | Respectively load AC voltage by 5?10?16 times rared power for 5 minutes. | No visible flame |
Typical Applications
Many properties of metal oxide film resistors are similar to metal film resistors. For basic use, metal film and metal oxide film are currently the predominant resistor types. Compared to carbon film, the prices are just as low. Only for dissipation values above 1 watt combined with reasonable stability, the carbon film resistors are still more cost efficient.
Construction
The metal oxide film is mostly produced with chemical deposition methods. Almost always a ceramic carrier is used as substrate. The deposition process involves the reaction of a pure metal with a gas at high temperature and at a low pressure. A very common metal oxide film is tin oxide. The film is established by heating the resistor body in a tin chloride vapor. Other metal oxide films have usually a different deposition process. Firstly a thin metal film is applied, which is afterwards reacted with oxygen. The desired composition is achieved by measuring the resistance of a test piece.
After the film is applied to the resistor body, the final resistance value is achieved by applying a helical cut. This is usually done by laser cutting, while in the past it was done by grinding or sandblasting. The spiral cut makes the resistance path longer and of smaller cross section, and can increase the resistance value up to thousand times greater than before the cut. The resistance value can be accurately controlled by the cutting. During the cutting process, the resistance is measured to allow for small corrections.
History
Metal oxide film resistors were the first alternatives to carbon composition resistors. They were in the past easier to manufacture than metal film resistors. Nowadays however, their numbers decrease and they are less and less available.
Product Detail
Basic Info
Product Description
Our factory manufacture many kinds of Metal Oxide Film Fixed Resistors, 1/6w, 1/4w, 1/2w, 1w, 2w, 3w. We can provide low price about resistor.
Feature:
1.Good performance in moisture resistance, anti-oxidization, good thermal stability, nonflammability, overload stability.
2.perating ambient temperature: -55?~+155?.
3.The surface is nonflammable, the normal size coating is brick red and the smalli size coating is green.
4.Resistance tolerance:±2%?±5%.
- High Precision Metal Film Resistors 1 Pieces / (Min. Order)
- Nonflammable Metal Film Fixed Resistors 1 Pieces / (Min. Order)
- High Precision Metal Film Fixed 5 Bands 50 Ohm 250 Ohm 350 Ohm Resistor with 0.1% Resistance Tolerance 1 Pieces / (Min. Order)
- 2 W 5W 22M 1ohm Color Coding Metal Film Fixed Resistors With 5% Resistance Tolerance 1 Pieces / (Min. Order)
- 10M 100 Megohm Pull Down Nonflammable LCR HCR High Voltage Carbon Fixed Film Resistors LCR HCR High Voltage Carbon Fixed Thin Film Resistors 1 Pieces / (Min. Order)
- 1/8W 1/4W 1/2W 1W 2W 3W 5WColor Coding Formula Thin Layer 2% 5% 10% Carbon Film Resistors 1 Pieces / (Min. Order)